Alathon® M5363
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SMA0HC_Alathon-M5363.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ALATHON M5363 is a high density copolymer with a narrow molecular weight distribution. This resin provides high impact strength and stress crack resistance, excellent color, low odor and good processability. Typical applications include open head pails, large shipping containers and 55-gallon drum lids. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.53 to 0.59 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.5 | g/10 min | ASTM D1238 |
| Spiral Flow | 22.6 | cm | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| -- | 1030 | MPa | |
| 1% Secant | 809 | MPa | |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 28.1 | MPa | |
| Break | 24.1 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 8.5 | % | |
| Break | 1500 | % | |
| Flexural Modulus 4 | ASTM D790 | ||
| -- | 1440 | MPa | |
| 1% Secant | 1290 | MPa | |
| 2% Secant | 1070 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 45 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 74.0 | °C | ASTM D648 |
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 126 | °C | ASTM D1525 |
| Peak Melting Temperature | 130 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 117 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 13 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Sanalite® PPH | Quadrant Engineering Plastic Products | PP Homopolymer | Quadrant EPP |
| Spartech Polycom PP5150 | Spartech Polycom | PP Homopolymer | Spartech |
| Ultramid® SEG8 GY7716B | BASF Corporation | Nylon 6 | Ultramid® |
| NORYL™ ENG265 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Hifax TYC 852X | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |