ASTADUR™ B5530
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTADUR™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SLmnl0_ASTADUR-B5530.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTADUR™ B5330 is a high strength grade of Polybutylene Terephthalate (PBT) polymer. It has excellent processability, high rigidity good dimensional stability and is resistant to chemical attack. Note: The letters "UV" indicate UV stabilisation has been added [ ie: ASTADUR™ B5530UV ]. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 58.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 130 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 87.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 60 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | > 85.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 160 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 60.0 | °C | |
| Vicat Softening Temperature | 200 | °C | ASTM D1525 5 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Processing (Melt) Temp | 230 to 270 | °C | |
| Mold Temperature | 70.0 to 120 | °C | |
| Injection Pressure | 40.0 to 130 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.200 to 0.350 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2207 HF UP | RTP Company | PEEK | RTP |
| SEETEC LLDPE UF917 | Lotte Chemical Corporation | LLDPE | SEETEC LLDPE |
| Sumitomo PP Y101 | Sumitomo Chemical Asia | PP Homopolymer | Sumitomo PP |
| Hostacom TRC 453N E | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ THERMOCOMP™ RC003 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ THERMOCOMP™ |