FM® 400NA

Category:	Epoxy , Epoxy; Epoxide
Manufacturer:	Cytec Industries Inc.
Trademark:	FM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	SK3PP2_FM-400NA.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
FM® 400NA adhesive film is the non-asbestos version of FM 400 and is designed to provide similar performance to that of FM 400 adhesive across the board. It is supplied with a lightweight nylon carrier and is designed for bonding metal-to-metal and sandwich composite structures requiring long time exposures to 420°F (216°C). BR® 400 is a modified epoxy corrosion inhibiting primer and provides excellent corrosive resistance when used on aluminum structures. FM 400NA adhesive film will also bond to BR® 127 primer with normal results. Where corrosion resistance is not required, FM 400NA adhesive film can be used without primer. FM 400NA adhesive film can be cured over a wide range of heat-up rates, temperatures and pressures. The recommended cure cycle is a 3 to 8.5°F/min (1.6 to 4.7°C/min) heat-up rate with a 60 minute hold at 350 ± 10°F (177 ± 5.6°C) and 45 ± 10 psi (0.31 ± 0.07 MPa) pressure. Suggested Appliations: Honeycomb sandwich construction Metal-to-metal bonding

Message

FM® 400NA adhesive film is the non-asbestos version of FM 400 and is designed to provide similar performance to that of FM 400 adhesive across the board. It is supplied with a lightweight nylon carrier and is designed for bonding metal-to-metal and sandwich composite structures requiring long time exposures to 420°F (216°C). BR® 400 is a modified epoxy corrosion inhibiting primer and provides excellent corrosive resistance when used on aluminum structures. FM 400NA adhesive film will also bond to BR® 127 primer with normal results. Where corrosion resistance is not required, FM 400NA adhesive film can be used without primer. FM 400NA adhesive film can be cured over a wide range of heat-up rates, temperatures and pressures. The recommended cure cycle is a 3 to 8.5°F/min (1.6 to 4.7°C/min) heat-up rate with a 60 minute hold at 350 ± 10°F (177 ± 5.6°C) and 45 ± 10 psi (0.31 ± 0.07 MPa) pressure.

Suggested Appliations:
Honeycomb sandwich construction
Metal-to-metal bonding

General Information
Features	Good Adhesion Good Corrosion Resistance Good Thermal Aging Resistance High Heat Resistance
Uses	Adhesives Bonding Structural Parts
Appearance	Grey
Forms	Film

Mechanical	Nominal Value	Unit
Flexural Strength ¹	6.62	MPa
Shear Strength
24°C ²	26.4	MPa
24°C ³	23.4	MPa

Additional Information	Nominal Value	Unit
Volatiles	< 2.0	%

Note Message
1 .	FM 400 film, 0.10 psf (0.50 kg/m²) with BR 400 primer, bonded honeycomb panels
2 .	FM 400NA film with BR 400 primer, 0.050 in. (1.27 mm) Ti6-4V annealed titanium substrates
3 .	FM 400NA film with BR 400 primer, 2024-T81 bare aluminum substrates

Resin Grade	Manufacturer	Category	Trademark
RTP 703	RTP Company	HDPE	RTP
Yuyao PP TL902	Yuyao Tenglong Plastics Co., Ltd.	PP, Unspecified	Yuyao PP
Zhongfa PP pp10	Yuyao Zhongfa Engineering Plastics Co. Ltd.	PP, Unspecified	Zhongfa
LNP™ LUBRICOMP™ UFL36S compound	SABIC Innovative Plastics Asia Pacific	PPA	LNP™ LUBRICOMP™
Sylvin 8240-80FU White 1508	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin