Wechat:
| Message |
|---|
| HiFill®PA6/6 CM40 6122 BK is a polyamide 66 (nylon 66) product, which contains a 40% mineral filler. It can be processed by injection molding and is available in North America. The main characteristics are: heat stabilizer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.70 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 121 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 86.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 5650 | MPa | ASTM D790 |
| Flexural Strength | 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 320 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 124 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 115 | °C | ASTM D648 |
| CLTE - Flow | 7.2E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 18 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Rear Temperature | 282 - 293 | °C | |
| Middle Temperature | 288 - 299 | °C | |
| Front Temperature | 277 - 288 | °C | |
| Nozzle Temperature | 282 - 293 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 54.4 - 93.3 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well ventedMoisture Content, as received: Product is packaged at 0.2% or less.Recomended Max Moisture: 0.12% down to 0.08% |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong Nylon PA1212BR-3 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon, Unspecified | Shandong Nylon |
| Sinvicomp SRP3613A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Nylene® 9533 | Custom Resins Group | Nylon 612 | Nylene® |
| Daelim Po1y® LL-34H | DAELIM INDUSTRIAL CO., LTD. | LLDPE | Daelim Po1y® |
| Petrotene® PP A2 T30 PRTA011 PH201 | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |