Menzolit® SMC 0410
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Menzolit Ltd (UK) |
| Trademark: | Menzolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SIcdfQ_Menzolit-SMC-0410.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Menzolit® SMC 0410 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is a must to work with chrome plated tools. The product contains no halogens nor heavy metals. Menzolit® SMC 0410 is a Premium Class-A SMC for on-line painted exterior body applications on cars developed with CCC technology. These compounds mould to parts with excellent surface quality for on-line painted body panels at high bake temperatures (190- 200 °C). The parts have to be primed with a conductive primer before e-coating. Moulded parts comply with all regulations of the automotive industry including low C-emissions. Surface defects like waviness, fibre patterns and orange peel are not existent with this product. To achieve the highest surface quality, we recommend that tool surfaces are mirror polished. The parts show very good adhesion to paint or In Mould Coating (IMC). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.90 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| -- 1 | 0.0 | % | DIN 53464 |
| -- | -0.050 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | < 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 12000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, Compression Molded) | 1.5 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 11000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 190 | MPa | ISO 178 |
| Compressive Stress | 100 | MPa | ISO 14126 |
| Poisson's Ratio | 0.30 | Internal Method | |
| Matrix Crazing Strain | 0.40 | % | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Compression Molded) | 86 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Continuous Use Temperature | 165 | °C | Internal Method |
| Glass Transition Temperature | 200 | °C | DSC |
| CLTE - Flow | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 145 to 155 | °C | |
| Injection Pressure | 8.00 to 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Post Molding Shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN AE8000 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| PROTEQ™ H24ST8 | Marplex Australia Pty. Ltd. | PP Homopolymer | PROTEQ™ |
| Sasol Polymers PE HF123 | Sasol Polymers | LLDPE | Sasol Polymers PE |
| SILVER® PP 423G10 | Guangdong Silver Age Sci & Tech. Co., Ltd | PP, Unspecified | SILVER® |
| Sylvin 8805-95FR BROWN 7153 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |