Evoprene™ 3275
| Category: | SBS , Styrene Butadiene Styrene Block Copolymer |
| Manufacturer: | AlphaGary |
| Trademark: | Evoprene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SIKdCg_Evoprene-3275.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The Evoprene™ Standard series is based mostly on SBS (styrene-butadiene -styrene) block copolymer rather than the hydrogenated SEBS type. This is a lower cost polymerso these grades are generally available at reduced cost compared with the Evoprene™ G or GC grades. SBS is the block copolymer form of SBR rubber and the properties generally mirror those of its vulcanisable cousin. Compounds produced from SBS block copolymer are suitable for a wide range of applications including extruded door, window and furniture seals and rubbing strips, mats, bump stops, grommets, coat hanger pads, toy components etc. Compounds remain flexible to very low temperatures (-60°C, - 75°F) and can be used at up to +55 - 60°C (130 - 140°F). A wide range of hardnesses is available from the mid 20s Shore A to about 60 Shore D. Many compounds are formulated for good ozone resistance but whilst grades pigmented black can be used for external application non black grades will quickly harden and discolour outside. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 2782 |
| Molding Shrinkage | 0.50 to 1.2 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 40 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 1.40 | MPa | ISO 37 |
| Tensile Stress (Yield) | 5.20 | MPa | ISO 37 |
| Tensile Elongation (Break) | 830 | % | ISO 37 |
| Tear Strength 1 | 30 | kN/m | ISO 34-1 |
| Compression Set (22°C, 72 hr) | 35 | % | ISO 815 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| M-S Flow | 0.883 | MPa | Internal Method |
| Ozone Resistance 2 | crack | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 160 to 180 | °C | |
| Front Temperature | 160 to 180 | °C | |
| Nozzle Temperature | 150 to 170 | °C | |
| Processing (Melt) Temp | 220 | °C | |
| Mold Temperature | 15.0 to 30.0 | °C | |
| Injection Rate | Fast | ||
| Vent Depth | 0.020 to 0.050 | mm |
| Note Message | |
|---|---|
| 1 . | Method Ba, Angle (Unnicked) |
| 2 . | 100 pphm, 20%str |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3583 | RTP Company | FEP | RTP |
| Mirakutoran® TPU E595 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Toyolac® 834V-X01 | Toray Resin Company | ABS | Toyolac® |
| Torelina® A310MX04 | Toray Resin Company | PPS | Torelina® |
| Tritan™ MX710 | Eastman Chemical Company | Copolyester | Tritan™ |