AKROMID® B3 F0 natural (1812)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SE87VT_AKROMID-B3-F0-natural-1812-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 F0 natural (1812) is an nonreinforced polyamide 6 with halogen- and phosphorusfree flame retardant, listed acc. UL 94 at 0,8 mm in all colours, meeting the demand high GWIT of the appliances industry. This material is listet at VDE. Application areas are housings, fasteners and cable connectors in the electro- and electronic industry |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.17 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.80 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.7 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4000 | 1300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 77.0 | 42.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield | 3.5 | 22 | % | |
| Break | 12 | > 100 | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | > 100 | -- | kJ/m² | |
| 23°C | > 100 kJ/m² | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 180 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 222 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.800 mm) | 775 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 38 | -- | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 2477 | Teknor Apex Company | TPV | Sarlink® TPV |
| Starflam PK0069 | Eurostar Engineering Plastics | Nylon 6 | Starflam |
| Nypol® PA A3 G30 HS UV PRTA011 NR395 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Adell Polyamide AW-77 | Adell Plastics, Inc. | Nylon 66/6 | Adell Polyamide |
| LNP™ THERMOCOMP™ GF003 compound | SABIC Innovative Plastics | PSU | LNP™ THERMOCOMP™ |