AKROMID® C3 ICF 30 5 XTC black (5473)
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SDpK0L_AKROMID-C3-ICF-30-5-XTC-black-5473-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® C3 ICF 30 5 XTC black (5473) is a 30% carbon fibre reinforced, high heat stabilised polyamid 66/6 blend with high flexural strength, good sliding properties and extra high temperature tolerance. Applications are mechanically high stressed parts in all industries |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.28 | -- | g/cm³ | ISO 1183 |
| Humidity Absorption - 62% RH (70°C) | 2.3 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 2.0 | 3.8 | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 25000 | 10200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 210 | 120 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.5 | 3.8 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 21500 | 10700 | MPa | ISO 178 |
| Flexural Stress 3 | 320 | 200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | -- | kJ/m² | |
| 23°C | 7.0 | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | -- | kJ/m² | |
| 23°C | 45 | 54 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 4 | 260 | -- | °C | DIN EN 11357-1 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-8800 FR | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| Shuman ABS 730H | Shuman Plastics, Inc. | ABS | Shuman ABS |
| Akulon® S223-HPG5 | DSM Engineering Plastics | Nylon 66 | Akulon® |
| Chiao Fu PA66 MD312LB30 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| Grivory® HTV-3H1 nat | EMS-GRIVORY | Nylon 6I/6T | Grivory® |