LNP™ LUBRICOMP™ DP003 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SDGPLG_LNPLUBRICOMPDP003compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* DP003 is a compound based on Polycarbonate resin containing Silicone, PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound DL-4530 Product reorder name: DP003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.90 - 1.0 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.0 - 1.2 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.0 - 1.2 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.80 - 1.0 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.19 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2230 | MPa | ASTM D638 |
| -- | 2170 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 49.0 | MPa | ASTM D638, ISO 527-2 |
| Fracture | 42.7 | MPa | ASTM D638 |
| Fracture | 41.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 5.6 | % | ASTM D638 |
| Yield | 5.8 | % | ISO 527-2 |
| Fracture | 35 | % | ASTM D638 |
| Fracture | 41 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1900 | MPa | ASTM D790 |
| -- | 1840 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 75.8 | MPa | ASTM D790 |
| -- | 75.2 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.10 | ASTM D3702 Modified | |
| With Self-Static | 0.26 | ASTM D3702 Modified | |
| Wear Factor - Washer | 42.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 280 | J/m | ASTM D256 |
| 23°C 2 | 32 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 28.4 | J | ASTM D3763 |
| -- | 61.5 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 128 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 3 | 129 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 304 - 316 | °C | |
| Front Temperature | 310 - 321 | °C | |
| Processing (Melt) Temp | 299 - 316 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene T20P250-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Tempalux® Medical | Westlake Plastics Company | PEI | Tempalux® |
| VITAMIDE® BG35BK6357 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| NuSil MED3-4013 | NuSil Technology | Silicone | NuSil |
| OmniTech™ ABS GR10 | OMNI Plastics, LLC | ABS | OmniTech™ |