Polytron® P40B07
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | Polytron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SBHRt5_Polytron-P40B07.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A chemically coupled 40% LGF reinforced black PP, heat stabilized, UV stabilized for injection moulding applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.12 | % | ASTM D955 |
| -- | 0.12 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 120 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 8200 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 190 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 22 | kJ/m² | ISO 179 |
| 23°C | 19 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 60 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 190 | J/m | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 18 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 156 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 168 | °C | ISO 11357-3, ASTM D3417 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Flammability | 22 | mm/min | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 - 220 | °C | |
| Middle Temperature | 200 - 225 | °C | |
| Front Temperature | 205 - 230 | °C | |
| Mold Temperature | 30.0 - 65.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 35.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® 450Y MH1 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| ADDILENE H 220 T20 | ADDIPLAST | PP Homopolymer | ADDILENE |
| Dugdale PVC Dynamic PVC Nitrile Flexible Compound | Dugdale Plc | PVC, Flexible | Dugdale PVC |
| Huafon JF-S-PV8300 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Axiall PVC 7255 | Axiall Corporation | PVC, Rigid | Axiall PVC |