SEETEC EVA EF321
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | SEETEC EVA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S7wYRy_SEETEC-EVA-EF321.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Application Agricultural Film Feature
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.928 to 0.932 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 to 1.2 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 2% Secant 2 | 63.7 | MPa | ASTM D638 |
| Tensile Strength 3 | ASTM D638 | ||
| Across Flow : Break | 30.4 | MPa | |
| Flow : Break | 30.4 | MPa | |
| Break | 19.6 | MPa | |
| Tensile Elongation 4 | |||
| Break 5 | 650 | % | ASTM D638 |
| Break 6 | 400 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dart Drop Impact | > 400 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 220 | g | |
| TD | 260 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 |
| Peak Melting Temperature 7 | 94.0 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 105 | ASTM D2457 | |
| Haze | 3.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Condition: 23°C |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | 500 mm/min |
| 5 . | Across Flow |
| 6 . | Flow |
| 7 . | Condition: 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resiprene® 1065 | Resirene, S.A. de C.V. | TPE | Resiprene® |
| Selvol™ E 203S | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| EPO-TEK® EJ2189-LV | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| KOPET® KP133G30BL | Kolon Plastics, Inc. | PET | KOPET® |
| Iupital® FX-11J | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |