POLYpropen PPC 12000
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYpropen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S7Fcpr_POLYpropen-PPC-12000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP copolymer |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.5 to 1.8 | % | |
| Flow | 1.5 to 1.8 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 25.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 6.0 | kJ/m² | |
| 23°C | 10 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed) | 56.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 146 | °C | ISO 306/A50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 7868-95C Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 2936-80 White 1505 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Nipol® BR 1220SB | Zeon Corporation | PBR, High Cis | Nipol® BR |
| Axiall PVC 4900 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Karina COMP. PVC BRANCO -E 703D10/ 58-H-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |