Sup-tech A709
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Shanghai Suptech Engineering Plastics Co. Ltd. |
| Trademark: | Sup-tech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S6rHtd_Sup-tech-A709.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sup-tech A709 is a Polyamide 66 (Nylon 66) product filled with 45% glass fiber. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | DIN 53479 |
| Molding Shrinkage | 1.0E-3 to 5.0E-3 | % | DIN 53464 |
| Water Absorption | DIN 53495 | ||
| 23°C, 24 hr | 0.60 | % | |
| Saturation, 23°C | 5.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 195 | MPa | DIN 53455 |
| Tensile Strain (Break) | 3.0 | % | DIN 53452 |
| Flexural Modulus | 11000 | MPa | DIN 53457 |
| Flexural Stress | 245 | MPa | DIN 53457 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 13 | kJ/m² | DIN 53453 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | DIN 53461 | ||
| 0.45 MPa, Unannealed | 258 | °C | |
| 1.8 MPa, Unannealed | 252 | °C | |
| Melting Temperature | 260 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Electric Strength | 20 | kV/mm | DIN 53481 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 6.0 to 10 | hr | |
| Processing (Melt) Temp | 260 to 300 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hifax TRC 298P | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| Iupiace® LN91 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| LNP™ VERTON™ MV006SU compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |
| Pro-fax SC973 | LyondellBasell Industries | PP Impact Copolymer | Pro-fax |
| LNP™ LUBRICOMP™ KL004L compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |