Flexirene® CM 50
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Flexirene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S6k17C_Flexirene-CM-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flexirene CM 50 is a butene copolymer with medium density (C4-LLDPE), with antioxidants, suitable for cast film extrusion. Main Application Flexirene CM 50 is a highly stiff product and it is recommended for the production of coextruded stretch film in slip-cling formulations where it acts as slip layer. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.1 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Cast Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Film Thickness - Recommended / Available | 10 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 23 µm, Cast Film | 350 | MPa | |
| 1% Secant, TD : 23 µm, Cast Film | 370 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 23 µm, Cast Film | 17.0 | MPa | |
| TD : Yield, 23 µm, Cast Film | 16.0 | MPa | |
| MD : Break, 23 µm, Cast Film | 25.0 | MPa | |
| TD : Break, 23 µm, Cast Film | 20.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 23 µm, Cast Film | 600 | % | |
| TD : Break, 23 µm, Cast Film | 700 | % | |
| Dart Drop Impact 1(23 µm, Cast Film) | 45 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 23.0 µm | 8.0 | kN/m | |
| TD : 23.0 µm | 20.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 118 | °C | ISO 306/A |
| Melting Temperature | 127 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 23.0 µm, Cast Film) | 75 | ASTM D2457 | |
| Haze (23.0 µm, Cast Film) | 8.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 to 270 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 7868-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Etinox® EK-8800 | Ercros, S.A. | PVC, Flexible | Etinox® |
| Duratuf™ 809 | Technical Polymers, LLC | Acetal (POM) Copolymer | Duratuf™ |
| Hifax DBS 189 D | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| Karina CLEAR PVC COMPOUND 80/223-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |