SLOVALEN® PC 13 T 30
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Plastcom |
| Trademark: | SLOVALEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S6Ik25_SLOVALEN-PC-13-T-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Modified copolymer PP for injection moulding or extrusion parts with the content of 30 % mineral filler. Increased rigidity, strength and impact strenght.Delivered in natural mode and in the full RAL colour scale. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 1.2 | % | |
| Flow | 1.3 | % | |
| Water Content | < 0.20 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2750 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 20 | % | ISO 527-2 |
| Flexural Modulus | 2550 | MPa | ISO 178 |
| Flexural Stress | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 3.0 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 16 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 65.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 153 | °C | ISO 306/B |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 550 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 200 to 250 | °C | |
| Mold Temperature | 40.0 to 50.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Faraprene 200 | Primex Plastics Corporation | TPE Alloy | Prime Faraprene |
| TYNEP® P4300 | Tyne Plastics LLC. | PBT | TYNEP® |
| PENTAMID A E20 H schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| POCAN® ECO T 3215 000000 | LANXESS GmbH | PBT+PET | POCAN® |
| SQUARE® LSR6050-50JT | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |