Order Products : sales@su-jiao.com
ADVANCENE™ bEE-4909-AAH
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | ETHYDCO |
| Trademark: | ADVANCENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S5lVFS_ADVANCENEbEE4909AAH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADVANCENE™ bEE-4909-AAH is a bimodal high molecular weight high density ethylene-hexene copolymer, produced using Advanced Gas phase PE Process in a single reactor. Its high molecular weight, bimodal molecular weight distribution and optimum density results in films with high strength, high rigidity and excellent processability. Tubular films of ADVANCENE™ bEE-4909-AAH resin are recommended for high strength grocery sacks, shopping bags and other thin film applications. The combination of strength, toughness and drawdown makes this resin ideal for downgauging in many applications. Films are readily treated and printed to give high-quality graphics. ADVANCENE™ bEE-4909-AAH resin is compatible with color concentrates, thus permitting the production of a variety of colored films that serve as protective and attractive decorative wraps. Main Charactenstlcs:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.949 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 9.0 | g/10 min | ASTM D1238, ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 13 | µm | |
| Film Puncture Energy 1 | 0.940 | J | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 13 µm | 32.0 | MPa | ASTM D882 |
| TD : Yield, 13 µm | 30.0 | MPa | ASTM D882 |
| MD : Broken, 13 µm | 71.0 | MPa | ASTM D882 |
| TD : Broken, 13 µm | 68.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 13 µm | 350 | % | ASTM D882 |
| TD : Broken, 13 µm | 350 | % | ASTM D882 |
| Dart Drop Impact (13 µm) | 260 | g | ASTM D1709A, ISO 7765-1 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 13 µm 2 | 11 | g | ASTM D1922 |
| TD : 13 µm | 24 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 130 | °C | ASTM D3418, ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 215 | °C |
| Note Message | |
|---|---|
| 1 . | Univation Method |
| 2 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4650 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Purell PE 3220 D | LyondellBasell Industries | LDPE | Purell |
| Anjatech® R250-DT2/GF30 | Almaak International GmbH | Nylon 6 | Anjatech® |
| Colorite Rigid PVC 1127A-012 | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| CP PRYME® Nylon 66 NN333HSL BK-P | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |