LNP™ THERMOCOMP™ DF002ERH compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S3hxMN_LNP-THERMOCOMP-DF002ERH-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* DF002ERH is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Easy Molding, Healthcare, Mold Release. Also known as: LNP* THERMOCOMP* Compound DF-1002 EM MR HC Product reorder name: DF002ERH |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.27 | g/cm³ | ISO 1183 |
| -- | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.51 | % | ISO 294-4 |
| Flow : 24 hr | 0.43 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4170 | MPa | ASTM D638 |
| -- | 4100 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 83.4 | MPa | ASTM D638 |
| Break | 84.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.8 | % | ASTM D638 |
| Break | 3.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 4280 | MPa | ASTM D790 |
| -- | 3920 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 149 | MPa | ASTM D790 |
| -- | 117 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 98 | J/m | ASTM D256 |
| 23°C 2 | 8.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 930 | J/m | ASTM D4812 |
| 23°C 3 | 62 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 13.4 | J | ASTM D3763 |
| -- | 9.24 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 141 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 141 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 137 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 137 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 3.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 5.3E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 5.4E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP EI5003L | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Sylvin 6208-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| AIE PC 10G4 | Asia International Enterprise (Hong Kong) Limited | PC | AIE PC |
| INEOS LLDPE LL6910AA | INEOS Olefins & Polymers Europe | LLDPE | INEOS LLDPE |
| Hostacom HBG H01 BLACK | LyondellBasell Industries | PP Homopolymer | Hostacom |