Plaslube® J-1/30/TF/13/SI/2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S3FNFM_Plaslube-J-1-30-TF-13-SI-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube®J-1/30/TF/13/SI/2 is a polyamide 66 (nylon 66) product containing a 30% glass fiber reinforced material. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | ||||
| -- | 1.49 | -- | g/cm³ | ASTM D792 |
| -- | 1490 | -- | kg/m³ | ISO 1183 1 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | -- | % | ASTM D955 |
| Water Absorption | ||||
| 24 hr | 0.50 | -- | % | ASTM D570 |
| Saturation | 5.3 | -- | % | ISO 62 2 |
| Balance | 1.4 | -- | % | ISO 62 3 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | 7200 | MPa | ISO 527-2 4 |
| Tensile Stress | ||||
| Fracture | 155 | 130 | MPa | ISO 527-2 5 |
| 23°C | 162 | -- | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Fracture, 23°C | 2.5 | -- | % | ASTM D638 |
| Fracture | 2.5 | 4.5 | % | ISO 527-2 6 |
| Flexural Modulus (23°C) | 9450 | -- | MPa | ASTM D790 |
| Flexural Strength (23°C) | 241 | -- | MPa | ASTM D790 |
| Compressive Strength | 165 | -- | MPa | ASTM D695 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA 7 | |||
| -30°C | 7.00 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 10.0 | 18.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 3.18 mm) | 96 | -- | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa | 260 | -- | °C | ISO 75-2 8 |
| 1.8 MPa, not annealed | 254 | -- | °C | ASTM D648 |
| 1.8 MPa | 250 | -- | °C | ISO 75-2 9 |
| Melting Temperature 10 | 260 | -- | °C | ISO 11357-3 11 |
| CLTE - Flow | 4.3E-5 | -- | cm/cm/°C | ASTM D696 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.59 mm) | HB | -- | UL 94 | |
| Burning Behav. at 1.6mm nom. thickn. (1.50 mm, UL) | HB | -- | ISO 1210 12 |
| Additional Information |
|---|
| 干燥 Compressive Strength, ASTM D695, 73°F: 24000 psi |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.12 | % | |
| Rear Temperature | 282 - 293 | °C | |
| Middle Temperature | 288 - 299 | °C | |
| Front Temperature | 277 - 288 | °C | |
| Nozzle Temperature | 282 - 293 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 54.4 - 93.3 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well ventedMoisture Content, as received: Product is packaged at 0.2% or less.Recomended Max Moisture: 0.12% down to 0.08% |
| Note Message | |
|---|---|
| 1 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 2 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 3 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 4 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 5 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 6 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 7 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 8 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 9 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 10 . | 10 °C/min |
| 11 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| 12 . | ??????,?? ISO 10350 ??? 23°C/50%r.h. ??? |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3739 GRY 5129 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Cheng Yu PP225 | Cheng Yu Plastic Company Limited | PP, Unspecified | Cheng Yu |
| LUVOCOM® 1301-7178 | Lehmann & Voss & Co. | PPS | LUVOCOM® |
| HIFOR® LF1030AA | Westlake Chemical Corporation | LLDPE | HIFOR® |
| CERTENE™ PHM-20 | Muehlstein | PP Homopolymer | CERTENE™ |