KOPLA PA6 KNG1060
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | KOPLA Co., Ltd. |
| Trademark: | KOPLA PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S1lSmc_KOPLA-PA6-KNG1060.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPLA PA6 KNG1060 is a Polyamide 6 (Nylon 6) material filled with glass fiber. It is available in Asia Pacific. Primary attribute of KOPLA PA6 KNG1060: Flame Rated. Typical application of KOPLA PA6 KNG1060: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.70 to 1.2 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.5 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 123 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 4710 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 167 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 208 | °C | |
| 1.8 MPa, Unannealed | 204 | °C | |
| Melting Temperature | 220 | °C | |
| CLTE - Flow | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.80 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PE 4118P (18402) | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| Karina GRAY PVC COMPOUND 751-18/69-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 7833-80 Orange 547 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TechnoElast A 8000 I 1 nat | TechnoCompound GmbH | TPE | TechnoElast |
| 3M™ Dyneon™ PTFE Compound TFX R4262 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |