Generic PTT - Glass Fiber
| Category: | PTT , Polytrimethylene Terephthalate |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S1OMzA_Generic-PTT---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PTT - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 - 1.70 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.20 - 0.83 | % | ASTM D955 |
| 23°C | 0.20 - 0.90 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3100 - 16500 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 52.0 - 147 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 1.4 - 2.6 | % | ASTM D638 |
| Flexural Modulus (23°C) | 6190 - 9700 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 154 - 197 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 32 - 81 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 160 - 650 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 204 - 208 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 7.0E-6 - 3.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 6.7E-5 - 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (23°C) | 24 - 38 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C) | 4.00 | IEC 60250 | |
| Dissipation Factor (23°C) | 1.2E-3 - 0.016 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 650 - 703 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 675 - 728 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 127 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Processing (Melt) Temp | 246 - 260 | °C | |
| Mold Temperature | 95.0 - 105 | °C | |
| Injection Pressure | 86.0 - 86.2 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PTT - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S EGR1404 990 GRI | Radici Plastics | Nylon 6 | Radilon® |
| VITAMIDE® BF23GY6466 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Zhongfa PP DD2 1x102 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| ESENTTIA 03H82NA-TAR | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |
| Sylvin 8280-70UV White 1549 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |