DOMAMID® 66SN
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | DOMO Engineering Plastics SPA |
| Trademark: | DOMAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S1KqSX_DOMAMID-66SN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66, general purpose, for injection moulding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1(23°C, 72 hr) | 1.4 to 1.6 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 85.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 50 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 250 | °C | ISO 306/B50 |
| Melting Temperature | 258 to 262 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 750 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 to 3.00 mm) | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 285 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50% RH |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Fluorosint® 207 | Quadrant Engineering Plastic Products | PTFE | Quadrant EPP |
| Nypol® PA A3 G30 HS UV RH AMLA144 NR450 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Bakelite® UP 3415 | Hexion Inc. | Polyester, TS | Bakelite® |
| DURACON® AW-01LV | Polyplastics Co., Ltd. | Acetal (POM) Copolymer+PE | DURACON® |
| MAJORIS DW650 - 8229 | AD majoris | PP, Unspecified | MAJORIS |