POCAN® B 3216 HR 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS GmbH |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | S0epTX_POCAN-B-3216-HR-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 16 % glass fibers, injection molding, improved impact strength, hydrolysis stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.40 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 24.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Across Flow : 260°C, 2.00 mm 1 | 1.0 | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.10 | % | |
| Flow : 260°C, 2.00 mm 3 | 0.60 | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.7 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 5600 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | ||
| 3.5% Strain, 23°C | 160 | MPa | |
| 23°C 6 | 165 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 4.4 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT, GHMRW, 09-050, GF16 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 to 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 35 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | < 10 | kJ/m² | |
| 23°C | < 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 30 | kJ/m² | |
| 23°C | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 190 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 200 | °C | ISO 306/B120 |
| Melting Temperature 8 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 4.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.3E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (23°C, 1.00 mm) | 36 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 275 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RC Plastics RCPC 8 FR GF 10 | RC Plastics, Inc. (Div. of LNP Engineering Plastics) | PC | RC Plastics |
| Michilene F8200 | API Polymers, Inc. | PP Copolymer | Michilene |
| TOTAL Polystyrene Compound 856 | TOTAL Refining & Chemicals | PS (IRPS) | TOTAL Polystyrene |
| Diamond AES 177 | Network Polymers, Inc. | AES | Diamond AES |
| Flexalloy® 9300-80 | Teknor Apex Company | PVC Elastomer | Flexalloy® |