4DUR® 9K22130 FR1
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | 4Plas |
| Trademark: | 4DUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RzXhbP_4DUR-9K22130-FR1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4DUR 9K22130 FR1 is a Standard Flow 30% Glass Fibre Reinforced FR-V0 PBT |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Vertical flow direction | 1.0 | % | |
| Flow direction | 0.30 | % | |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.10 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH 1 | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11000 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 130 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 8.0 | kJ/m² | ISO 180/1A |
| 23°C | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 205 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | °C | ISO 306/B |
| Melting Temperature 2 | 225 | °C | ISO 11357 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Screw Speed | < 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 50 - 70 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Axiall PVC HR-5009 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Fainplast PVC PH 70/AS | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| GAPEKK™ 3200P | Gharda Chemicals Ltd. | PEKK | GAPEKK™ |
| RONFALIN® ASA 3323 U | A. Schulman Europe | ASA | RONFALIN® |
| Sylvin 9077-95C Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |