Centrex® 813
| Category: | ASA+AES , Acrylonitrile Styrene Acrylate + AES |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Centrex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RzQkfH_Centrex-813.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Centrex® 813 is an Acrylonitrile Styrene Acrylate + AES (ASA+AES) product. It can be processed by injection molding and is available in North America. Applications of Centrex® 813 include electrical/electronic applications, household applications, marine applications, outdoor applications and sporting goods. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2000 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 33.8 | MPa | ASTM D638 |
| Flexural Modulus - Tangent 3 | 1930 | MPa | ASTM D790 |
| Flexural Strength 4 | 54.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 53 | J/m | |
| 23°C, 3.18 mm | 410 | J/m | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Total Energy | 22.0 | J | |
| 23°C, Total Energy | 33.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.18 mm | 70.0 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 77.0 | °C | |
| Vicat Softening Temperature | 101 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 87.8 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 50 to 70 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 238 to 271 | °C | |
| Middle Temperature | 238 to 271 | °C | |
| Front Temperature | 238 to 271 | °C | |
| Nozzle Temperature | 238 to 271 | °C | |
| Processing (Melt) Temp | 238 to 271 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Injection Rate | Moderate-Fast | ||
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | 5.1 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCLAIR® FP120 Series | NOVA Chemicals | LLDPE | SCLAIR® |
| RMA 110/110F | Ronald Mark Associates, Inc. | PVC Copolymer | RMA |
| YUPLENE® R372Y | SK Global Chemical | PP Random Copolymer | YUPLENE® |
| Diaterm® B26 GF30V0 | DTR S.r.l. (Develop Thermoplastic Resins) | Nylon 66 | Diaterm® |
| MAXAMID™ PA66M32T-BK | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |