ENGAGE™ 8440
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RvMHs1_ENGAGE-8440.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™ 8440 Polyolefin Elastomer is an ethylene-octene copolymer that performs well in a wide range of thermoplastic elastomer applications. It is an excellent thermoplastic elastomer for blending and compounding. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.897 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.6 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 13 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 sec, Compression Molded | 86 | ||
| Shore D, 1 sec, Compression Molded | 36 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant 1(Compression Molded) | 6.30 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Compression Molded) | 20.4 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | 690 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : Compression Molded | 54.2 | MPa | |
| 2% Secant : Compression Molded | 54.3 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 78.9 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -33.0 | °C | Internal Method |
| Vicat Softening Temperature | 75.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) 5 | 93.0 | °C | Internal Method |
| Peak Crystallization Temperature (DSC) | 76.0 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A RV500K 100 NAT | Radici Plastics | Nylon 66 | Radilon® |
| SCHULAMID® 612 FS 5003 MC | A. Schulman Europe | Nylon 612 | SCHULAMID® |
| Witcom PC 2L1 | Witcom Engineering Plastics B.V. | PC | Witcom PC |
| APEX® 08-A0349A-83 NT NP | Teknor Apex Company | PVC, Flexible | APEX® |
| Forprene® 6NB901D40 | SO.F.TER. SPA | TPV | Forprene® |