SCHULAMID® 612 CS 4404
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RuircV_SCHULAMID-612-CS-4404.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High impact modified Polyamide 612 with heat stabilization and hydrolyse resistance |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.01 | -- | g/cm³ | ISO 1183/A |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1200 | 320 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 40.0 | 30.0 | MPa | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | > 200 | > 250 | % | ISO 527-2/1A/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 110 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 110 kJ/m² | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 70.0 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 55.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 200 | -- | °C | ISO 306/A50 |
| -- | 100 | -- | °C | ISO 306/B50 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 30 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | IEC 60695-11-10, -20 | |
| 3.00 mm | HB | -- | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | 725 | -- | °C | IEC 60695-2-12 |
| 3.00 mm | 725 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 750 | -- | °C | IEC 60695-2-13 |
| 3.00 mm | 750 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 干燥 ISO 1874-PA 612-EAGHLW-14-010-NDIN73378-PA 612-HIHL |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC PP R3400 | LG Chem Ltd. | PP Random Copolymer | SEETEC PP |
| Sumikon® FM-MK505 | Sumitomo Bakelite Co., Ltd. | PPS | Sumikon® |
| ALTECH® PA6 A 2015/327 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Arlon® 55LM | Arlon-MED | Epoxy | Arlon® |
| KOCETAL® K100HS | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |