HANWHA LLDPE 3325W
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RuTpqk_HANWHA-LLDPE-3325W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA LLDPE 3325W is manufactured by Spherilene process and designed for variety of film application such as protective film and stretch wrap film. LLDPE 3325W has well balanced property of mechanical property and processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.911 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 18.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 960 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 20 µm | 39.2 | MPa | ASTM D882 |
| TD : Break, 20 µm | 34.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 600 | % | ASTM D882 |
| TD : Break, 20 µm | 800 | % | ASTM D882 |
| Dart Drop Impact (20 µm) | 120 | g | ASTM D1709 |
| Tensile Tear Strength | ASTM D1004 | ||
| MD : 20.0 µm | 117.7 | kN/m | ASTM D1004 |
| TD : 20.0 µm | 122.6 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 96.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 121 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (20.0 µm) | 2.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 190 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 2 to 3Optimum Gage Range: 0.02 to 0.1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® FPP 30 GFC K1079 | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| Quadrant EPP Delrin® Acetal | Quadrant Engineering Plastic Products | Acetal (POM) Homopolymer | Quadrant EPP |
| Chiao Fu PA66/6 MB212GM33 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66/6 | Chiao Fu PA66/6 |
| Clariant Nylon 6/6 PA-113C | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| DINALON® B1S25 | Grupo Repol | Nylon 6 | DINALON® |