AKROMID® S3 GF 50 1 black (3441)
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ru2Lda_AKROMID-S3-GF-50-1-black-3441-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® S3 GF 50 1 black (3441) is a 50% glass fibre reinforced and heat stabilised polyamide 6.10 with very high stiffness and strength as well as lower moisture absorption and high chemical resistance. Applications are precision parts for apparatus engineering and precision mechanics as well as connectors, housings etc. in the automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.51 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 35.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.70 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 0.90 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 3.6 | -- | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 50 | -- | % | ISO 1172 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 230 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 14500 | 11000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 200 | 150 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | 4.5 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 13800 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 310 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 16 | -- | kJ/m² | |
| 23°C | 20 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 110 | -- | kJ/m² | |
| 23°C | 100 | 100 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 170 | -- | °C | ISO 75-2/C |
| Melting Temperature 4 | 220 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLPLAST TC 4000A | UTEKSOL d.o.o. | SBS | SOLPLAST TC |
| 3M™ Dyneon™ PTFE Compound TF 6220 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Andur 9500 APLF | Anderson Development Company | PUR-Ether/TDI | Andur |
| COSMOPLENE® Z432 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP, Unspecified | COSMOPLENE® |
| Sylvin 8250-70 Grey 9601 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |