Category: | Polyolefin, Unspecified , Polyolefin |
Manufacturer: | LyondellBasell Industries |
Trademark: | Hostacom |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | RthM74_Hostacom-TRC-452N-NAT.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
"Hostacom" TRC 452N NAT is a 20% mineral filled, impact modified grade for interior applications with excellent impact/stiffness balance, good flowability properties and excellent scratch resistance. It has an outstanding blooming resistance at elevated temperatures. The grade is the antistatic version of HC TRC 352N to avoid dust attraction. |
General Information | |
---|---|
Filler / Reinforcement |
|
Additive |
|
Features |
|
Uses |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 1.04 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ISO 1133 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Stress (Yield, 23°C) | 21.6 | MPa | ISO 527-2/50 |
Flexural Modulus 1(23°C) | 2000 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Charpy Notched Impact Strength | ISO 179/1eA | ||
-30°C | 4.5 | kJ/m² | |
23°C | 35 | kJ/m² | |
Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Heat Deflection Temperature (1.8 MPa, Unannealed) | 54.0 | °C | ISO 75-2/A |
Vicat Softening Temperature | 136 | °C | ISO 306/A50 |
Note Message | |
---|---|
1 . | 2.0 mm/min |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Next Nylon 6 Prime Series NX-01M.WH. | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
NOVAREX® 7025R | Mitsubishi Engineering-Plastics Corp | PC | NOVAREX® |
IDI STC 2154 | IDI Composites International | Vinyl Ester | IDI STC |
JSR EPR EBM2021P | JSR Corporation | EPDM | JSR EPR |
LNP™ STAT-LOY™ K3000Z compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ STAT-LOY™ |