Vipel® F737-PTT-30
| Category: | Polyester Alloy , Polyester Alloy |
| Manufacturer: | AOC, L.L.C. |
| Trademark: | Vipel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rtgh0D_Vipel-F737-PTT-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vipel Resilient Isophthalic Polyester Resin AOC's Vipel F737 series is a resilient isophthalic polyester resin with excellent mechanical properties. Vipel F737 resins are used extensively in grating and in the construction of large diameter water pipes for transporting water to and from power stations. Vipel F737 resins can be adapted for a variety of fabrication processes. Internationally Recognized Vipel F737 series resins have been used in many corrosion resistant applications such as grating and water pipes, etc. Corrosion Resistance This resin provides excellent corrosion resistance when used in contact with inorganic and organic acids. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. Versatile Suitable for various fabricating methods such as hand lay-up, spray-up, filament winding, etc. Food and Drug All resins in this datasheet are manufactured from raw materials that are listed in FDA regulation Title 21 CFR 177.2420. It is the fabricator's responsibility to also be sure that the final composite is well cured. All composites used for FDA applications should be post cured at 180°F/82°C for at least 4 hours. After post curing , laminate should be washed with soap and water and rinsed. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | |
| Styrene Content | 49 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Exotherm | |||
| Gel to Peak | 13.0 | min | |
| Peak | 192 | °C | |
| Gel Time (25°C) 1 | 30.0 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Thixotropic Index 2 | 3.00 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 39 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3380 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 85.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 3930 | MPa | ASTM D790 |
| Flexural Strength | 141 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 91.7 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Mix Viscosity 3(25°C) | 425 | cP | |
| Post Cure Time (82°C) | 4.0 | hr |
| Note Message | |
|---|---|
| 1 . | Gel time with 1.25% MEKP |
| 2 . | 6/60 rpm Thix Index |
| 3 . | Brookfield LV viscosity spindle 3 at 60 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Generic PC - Glass Fiber, Milled | Generic | PC | Generic |
| Globalene® 6331-11 | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| GXL 10003 | S&E Specialty Polymers, LLC | TPO (POE) | GXL |
| Kemcor LD 1434 | Qenos Pty Ltd | LDPE | Kemcor |
| KumhoSunny PBT 3710G | Shanghai KumhoSunny Plastics Co., Ltd. | PBT | KumhoSunny PBT |