Niform 270
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niform |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RtO1GL_Niform-270.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Acetalic copolymer with high MFI, suitable for the injection moulding of items having low thickness. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 27 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 2.4 - 2.9 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.40 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 64.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 30 | % | ASTM D638 |
| Flexural Modulus 3 | 2650 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 83.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.20 mm | 50 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 65 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 115 | °C | ASTM D648 |
| Vicat Softening Temperature | 150 | °C | ASTM D1525 5 |
| CLTE - Flow (23 to 55°C) | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 19 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.70 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Additional Information |
|---|
| Volume Resistivity, IEC 60093: >1E14 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermx® CGT33 | Celanese Corporation | PCT | Thermx® |
| Karina BLACK PVC COMPOUND 771-48/ 1-BY-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ RC004SXC compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ THERMOCOMP™ |
| Braskem PE SHC7260LS-L | Braskem America Inc. | HDPE | Braskem PE |
| Hifax TYC1175X Black | LyondellBasell Industries | TPO (POE) | Hifax |