LNP™ LUBRICOMP™ ZFL34 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RtDQI8_LNP-LUBRICOMP-ZFL34-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP ZFL34 is a compound based on PPE+PS resin containing 20% Glass Fiber, 15% PTFE. Added feature of this gradae is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound ZFL-4034 Product reorder name: ZFL34 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.40 to 0.60 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.060 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.070 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7210 | MPa | ASTM D638 |
| -- | 6820 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 96.4 | MPa | ASTM D638 |
| Yield | 91.5 | MPa | ISO 527-2/5 |
| Break 3 | 96.4 | MPa | ASTM D638 |
| Break | 91.5 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.9 | % | ASTM D638 |
| Yield | 1.9 | % | ISO 527-2/5 |
| Break 5 | 2.7 | % | ASTM D638 |
| Break | 1.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 6790 | MPa | ASTM D790 |
| -- 7 | 6440 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 137 | MPa | ISO 178 |
| -- | 137 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 135 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 135 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.44 | ||
| vs. Itself - Static | 0.59 | ||
| Wear Factor - Washer | 93.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 99 | J/m | ASTM D256 |
| 23°C 10 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 520 | J/m | ASTM D4812 |
| 23°C 11 | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 12.8 | J | ASTM D3763 |
| -- | 2.94 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 138 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 139 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 133 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 133 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 6.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 277 to 288 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 299 to 310 | °C | |
| Processing (Melt) Temp | 299 to 304 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 222 BLACK 1N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| ExxonMobil™ LLDPE LL 6201 Series Wire & Cable | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| Dynaflex™ G7930-9001-02 | PolyOne Corporation | TPE | Dynaflex™ |
| Leona™ 90G55 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Plenco 08122 (Compression) | Plastics Engineering Co. | Polyester, TS | Plenco |