Futerro® Injection
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Futerro |
| Trademark: | Futerro® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RsBSuA_Futerro-Injection.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Futerro® PLA injection grade is a thermoplastic resin derived from annually renewable resources and is specifically designed for injection molding applications where the requirements are clarity with heat deflection temperatures lower than 55°C. Futerro® PLA injection grade is easily processed on conventional injection equipment. The material is stable in the molten state, provided that the drying procedures are followed. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (25°C) | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 10 - 30 | g/10 min | ISO 1133 |
| 210°C/2.16 kg | 30 - 60 | g/10 min | ISO 1133 |
| Free Lactide Content | % | ||
| L-poly-Lactide Content | > 99 | % | |
| Moisture Content | ppm |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 60.0 | MPa | ISO 527-2 |
| Fracture | 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 3.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 52.0 - 60.0 | °C | ISO 11357-2 |
| Melting Temperature | 145 - 175 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm) | > 90.0 | % | ISO 14782 |
| Haze (2000 µm) | < 5.0 | % | ISO 14782 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density (230°C) | 1.08 - 1.12 | g/cm³ |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.025 | % | |
| Rear Temperature | 150 - 165 | °C | |
| Middle Temperature | 195 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 210 | °C | |
| Processing (Melt) Temp | 200 | °C | |
| Mold Temperature | 25.0 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 100 - 175 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 20°CFeed Temperature (Crystalline Pellets): 165°CFeed Temperature (Amorphous): 150°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5137-94 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| AKROMID® B3 GM 10/20 1 L black (4646) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| Cevian® SER241 | PlastxWorld Inc. | ABS | Cevian® |
| Kotex KG-30F15 | Kotec Corporation | PC | Kotex |
| Petro Rabigh PP FS2011E | Rabigh Refining & Petrochemical Co. | PP Homopolymer | Petro Rabigh PP |