Rilsan® RDG 179
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RrH0gb_Rilsan-RDG-179.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Rilsan® RDG 179 is a high molecular weight polyamide-11 pipe-grade resin developed to allow good dimensional control during pipe extrusion. RDG 179 is a heat and light stabilized, yellow grade of Rilsan polyamide 11 intended for use as high pressure natural gas distribution pipe. Rilsan RDG 179 is available in either 44 lb. foil lined bags or 1000 lb. foil lined containers to prevent moisture absorption during shipping, storage and handling. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ASTM D1248 |
| Water Absorption | Internal method | ||
| 23°C, 24 hr, 50% RH | 0.20 | % | Internal method |
| Saturation | 1.9 | % | Internal method |
| Equilibrium, 23°C, 50% RH | 0.80 | % | Internal method |
| Intrinsic Viscosity | 1.5 - 1.7 | dl/g | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fundamentals of Hydrostatic Design | ASTM D2837 | ||
| 23°C | 17.2 | MPa | ASTM D2837 |
| 60°C | 11.0 | MPa | ASTM D2837 |
| 80°C | 8.62 | MPa | ASTM D2837 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hoop Stress | 51.7 | MPa | ASTM D1599 |
| Hydrogen (H2) Gas Permeation (23°C) | 0.0698 | cm³·cm/cm²/sec/bar | Internal method |
| Methane (CH4) Gas Permeation (23°C) | 0.00220 | cm³·cm/cm²/sec/bar | Internal method |
| PENT 1 | 3000 | hr | ASTM F1473 |
| S4 Critical Pressure (0°C) | 0.552 | MPa | ASTM F1589 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 2 | 51.0 | MPa | ASTM D2290 |
| Yield | 39.3 | MPa | ASTM D638 |
| Fracture 3 | 40.0 | MPa | ASTM D2290 |
| Fracture | 42.7 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 14 | % | ASTM D638 |
| Fracture | 240 | % | ASTM D638 |
| Flexural Modulus | 1240 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 145 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 50.0 | °C | ASTM D648 |
| CLTE - Flow | ASTM D696 | ||
| -30 to 50°C | 8.5E-5 | cm/cm/°C | ASTM D696 |
| 10 to 49°C | 1.5E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Testing was performed on die cut samples from 2" SDR 11 extruded pipe produced under laboratory controlled conditions. Three sets of sample pipe was produced. The samples were chosen to span the resin manufacturing range of RDG 179. The raw data indicates that all samples from the three different sets are from the same population. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.060 | % | |
| Melt Temperature | 227 - 249 | °C |
| Note Message | |
|---|---|
| 1 . | No failures @ 80°C/2.4 MPa stress |
| 2 . | Apparent Tensile Strength |
| 3 . | Apparent Tensile Strength |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1481 N TFE 15 | RTP Company | PESU | RTP |
| Propilven J-901 | Propilven, S.A. | PP Homopolymer | Propilven |
| TAISOX 6810M | Formosa Plastics Corporation | LDPE | TAISOX |
| Jam HDPE HM CRP 100 Black | Jam Petrochemical Company | HDPE | Jam HDPE |
| Plexiglas® V045i | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |