Sumitomo Phenolic FM 4005
| Category: | Phenolic , Phenolic |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Sumitomo Phenolic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rqdnng_Sumitomo-Phenolic-FM-4005.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FM 4005 is a fiberglass reinforced phenolic novolac molding compound, with excellent dimensional stability and good strength at elevated temperatures. This material is compliant with the specifications of ASTM D 5948, Type MFH. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.77 | g/cm³ | ASTM D792 |
| Apparent Density | 0.80 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (Compression Molded) | 0.25 | % | ASTM D955 |
| Water Absorption - 48 hr | 0.23 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Compression Molded) | 75.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 15000 | MPa | ASTM D790 |
| Flexural Strength (Compression Molded) | 140 | MPa | ASTM D790 |
| Compressive Strength | 255 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 30 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, Compression Molded | 190 | °C | |
| 1.8 MPa, Annealed, Compression Molded | > 282 | °C | |
| CLTE - Flow | 1.9E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 150 | °C | UL 746 |
| RTI Imp | 150 | °C | UL 746 |
| RTI Str | 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | ASTM D149 | ||
| -- 2 | 10 | kV/mm | |
| -- 3 | 8.0 | kV/mm | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Wet, 60 Hz |
| 2 . | Method A (Short-Time) |
| 3 . | Method B (Step-by-Step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TP SD 333 60A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| UNITIKA Nylon 66 E-RUNG60 | UNITIKA Plastics Division | Nylon 66 | UNITIKA Nylon 66 |
| BESTPOLUX PCA-02 | Triesa Plastics | PC+ABS | BESTPOLUX |
| Gallonprene® GP520-3003 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| ELASTOSIL® RT 602 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® RT |