Nymax™ 600 A Natural 12
| Category: | Nylon 6 Alloy , Polyamide 6 Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Nymax™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rnio5V_Nymax-600-A-Natural-12.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon 6 Nymax®600 blend series products are "salt and pepper" pellet blends, including nylon resin, processing aids, performance modifiers and color masterbatches. According to different grades, these materials are dedicated to improving melt processing, component properties or surface morphology, and are economical substitutes for complete chemical products. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.1 - 1.3 | % | ASTM D955 |
| Water Absorption (24 hr, 3.18 mm) | 1.6 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2550 | MPa | ASTM D638 |
| Tensile Strength 1(Break) | 77.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 60 | % | ASTM D638 |
| Flexural Modulus | 2520 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 53 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 60.0 | °C | ASTM D648 |
| Melting Temperature | 215 | °C | ASTM D789 |
| Additional Information |
|---|
| Molded Test Bars: Dry as Molded |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Mold Temperature | 48.9 - 93.3 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALAT 37N000 - 8229 | AD majoris | PBT | MALAT |
| tefabloc® TP SD 300 60A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| Moplen EP203N | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| 3M™ Dyneon™ Fluoroelastomer FPO 3731 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| OTECH PVC OW135 - Automotive Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |