PPA FLAME RETARDANT COMPOUND
PPA, 30% GLASS FIBER REINFORCED, FLAME RETARDANT V0, PBB AND PBDE FREE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.67 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow : 23°C | 0.70 | -- | % | ISO 294-4 |
| Flow : 23°C | 0.20 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 2.5 | -- | % | ISO 62 |
| Saturated, 23°C | 0.20 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 12500 | 12500 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 180 | 170 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 | 2.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.5 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 38 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 40 | 40 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 6.5 | 6.5 | kJ/m² | ISO 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 1(1.8 MPa, Unannealed) | 280 | -- | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 130 | -- | °C | IEC 60216 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 3 | 1.0E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+17 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 24 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.40 mm | V-2 | -- | UL 94 | |
| 0.8 mm | V-0 | -- | UL 94 | |
| 1.6 mm | V-0 | -- | UL 94 | |
| 3.2 mm | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.8 mm | 960 | -- | °C | IEC 60695-2-12 |
| 3.2 mm | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.8 mm | 850 | -- | °C | IEC 60695-2-13 |
| 3.2 mm | 875 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | 20000 hr |
| 3 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8479-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen BA238A | PolyMirae | PP Copolymer | Moplen |
| Ultramid® T KR 4355 G7 | BASF Corporation | Nylon 6/6T | Ultramid® |
| LNP™ COLORCOMP™ D1000P compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |
| LNP™ LUBRICOMP™ MFL36S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ LUBRICOMP™ |