Telcar® TL-81-D965-P
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Telcar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RkkYva_Telcar-TL-81-D965-P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Telcar TL-81-D965-P is a general purpose, halogen-free thermoplastic elastomer designed for electrical applications requiring flexibility over a wide termperture range. Telcar TL-81-D965-P is a high durometer grade that is RoHS compliant and is suitable for both injection molding and extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 87 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412 | ||
| 100% strain, 0.508mm 2 | 5.00 | MPa | ASTM D412 |
| 300% strain, 0.508mm 3 | 6.34 | MPa | ASTM D412 |
| Tensile Strength (fracture, 0.508mm) | 12.1 | MPa | ASTM D412 |
| Tensile Elongation (fracture, 0.508mm) | 700 | % | ASTM D412 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (136°C, 168 hr) | 5.0 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (136°C, 168 hr) | -9.0 | % | ASTM D573 |
| Change in Tensile Strength (60°C, 168 hr, in IRM 902 Oil) | -72 | % | ASTM D471 |
| Change in Ultimate Elongation (60°C, 168 hr, in IRM 902 Oil) | -55 | % | ASTM D471 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Continuous Use Temperature | 105 | °C | ASTM D794 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 23°C | 3.1E+15 | ohms·cm | ASTM D257 |
| 50°C | 6.6E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength | 44 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 2.50 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ALL) | HB | UL 94 | |
| Oxygen Index | 18 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 - 193 | °C | |
| Middle Temperature | 177 - 199 | °C | |
| Front Temperature | 182 - 204 | °C | |
| Nozzle Temperature | 188 - 210 | °C | |
| Processing (Melt) Temp | 188 - 210 | °C | |
| Mold Temperature | 25.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 166 - 188 | °C | |
| Cylinder Zone 2 Temp. | 171 - 193 | °C | |
| Cylinder Zone 3 Temp. | 177 - 199 | °C | |
| Cylinder Zone 5 Temp. | 182 - 204 | °C | |
| Die Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | die cut from extruded tapes |
| 2 . | Mouth die C, 510mm/min |
| 3 . | C mold, 510mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 2862-63A | RTP Company | TPO (POE) | RTP |
| Novalloy-B B1300, B1300F | Daicel Polymer Ltd. | ABS+PBT | Novalloy-B |
| Compoceran H900-2 | Arakawa Chemical Industries, Ltd. | PAI | Compoceran |
| Hostacom TKC 406P NAT | LyondellBasell Industries | PP, Unspecified | Hostacom |
| Wanthane® WHT-1185EC | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |