BESTNYL SC50VIR34AHM
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ri89wh_BESTNYL-SC50VIR34AHM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 /6 lubrified with 50% glass fibre reinforcement, heat stabilized and Impact modified. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183 |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 185 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 80 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 230 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 215 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 235 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Dielectric Strength | 28 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Humidity Pellets, ISO 1110: 0.2%Flammability Speed, FMV 302:<100 mm/minAshes, Triesa Test: 30% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Processing (Melt) Temp | 270 - 280 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECOLITE KM-50BD | KYOCERA Chemical Corporation | Phenolic | TECOLITE |
| Zenite® 6140L | Celanese Corporation | LCP | Zenite® |
| Chemlon® A25 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Huafon JF-W-3026 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Hostacom HBG H02 BLACK | LyondellBasell Industries | PP Homopolymer | Hostacom |