RTP 4183
| Category: | PEKK , Polyetherketoneketone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ri4nvB_RTP-4183.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 to 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.12 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 25500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 276 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.9 | % | ASTM D638 |
| Flexural Modulus | 17200 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 379 | MPa | ASTM D790 |
| Compressive Strength | 262 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 800 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 288 | °C | ASTM D648 |
| Glass Transition Temperature | 156 | °C | ASTM E1356 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+5 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 357 to 399 | °C | |
| Middle Temperature | 357 to 399 | °C | |
| Front Temperature | 357 to 399 | °C | |
| Mold Temperature | 204 to 232 | °C | |
| Injection Pressure | 68.9 to 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 218G2 V30 BLACK 34 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Hanwha Total PP FH44 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| INNOPOL® PP CS 1-3820 MA | Inno-Comp Ltd. | PP Homopolymer | INNOPOL® PP |
| Karina OCHER PVC COMPOUND 810-37/3-CRB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lucon® PS6054 | LG Chem Ltd. | ABS | Lucon® |