Braskem PE SLL318
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RhhfVG_Braskem-PE-SLL318.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SLL318 is a Linear Low Density Polyethylene, copolymer of butene-1. Developed for cast film extrusion. Films obtained with this product show good mechanical properties and enhanced sealability. It contains antioxidant additives. The minimum biobased content of this grade is 87%, determined according to ASTM D6866. Applications: Stretch films; liners; LDPE and HDPE blends and packages for general use; blends for irrigation pipes; insulation for low and medium tension XLPE wires and cables. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.7 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 38 µm, Cast Film | 30.0 | MPa | |
| TD : Break, 38 µm, Cast Film | 30.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm, Cast Film | 1200 | % | |
| TD : Break, 38 µm, Cast Film | 1400 | % | |
| Flexural Modulus | ASTM D882 | ||
| 1% Secant, MD : 38 µm, Cast Film | 180 | MPa | |
| 1% Secant, TD : 38 µm, Cast Film | 200 | MPa | |
| Dart Drop Impact (38 µm, Cast Film) | 90 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, Cast Film | 120 | g | |
| TD : 38 µm, Cast Film | 340 | g |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 87 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3414 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Purell HP548N | LyondellBasell Industries | PP Homopolymer | Purell |
| Vydyne® R535J BK0701 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Fiberfil® J-60/20/TT/FD WT8381 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| IDI SMC 46-16-60 | IDI Composites International | TS, Unspecified | IDI SMC |