Bapolene® 122B
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Bamberger Polymers, Inc. |
| Trademark: | Bapolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RhKXR9_Bapolene-122B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bapolene LL122B is a general purpose LLDPE for blown film extrusion. This resin offers excellent tensile and toughness properties. Contains no slip and no antiblock additives. This product meets FDA standards for food contact applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 208 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 227 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield, 25 µm, blown film | 10.3 | MPa | ASTM D882 |
| TD : Yield, 25 µm, blown film | 10.5 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 38.7 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 28.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film 3 | 600 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film 4 | 800 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Blown Film) | 90 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 110 | g | ASTM D1922 |
| TD : 25 µm, blown film | 490 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (25.4 µm, Blown Film) | 35 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 19 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties are based on a thickness of 1.0 mil, blow-up ratio of 2.5:1 and 0.1 mm/mm-min Initial Strain Rate. |
| Note Message | |
|---|---|
| 1 . | 0.10 mm/min |
| 2 . | 0.10 mm/min |
| 3 . | 1.0 mm/min |
| 4 . | 0.10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 D TFE 20 | RTP Company | Nylon 612 | RTP |
| Tecolen® CP20 MF20 NL XC30 | Eurotec Engineering Plastics | PP Copolymer | Tecolen® |
| Unipren® Elastomers A3 PRTA010 80A EM06S1 UP336 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| NEXUS PC/ABS PC/ABSQX7005 | Nexus Resin Group, LLC. | PC+ABS | NEXUS PC/ABS |
| Fainplast PVC GK 01596 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |