Chemlon® 225-15 MGH
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rgxacw_Chemlon-225-15-MGH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Chemlon® 225-15 MGH is a Polyamide 6 (Nylon 6) material filled with 15% glass fiber and 25% mineral. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Chemlon® 225-15 MGH are:
Typical application of Chemlon® 225-15 MGH: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.15 to 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.90 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 128 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 2.5 | % | |
| Break | 2.5 | % | |
| Flexural Modulus | 7580 | MPa | ASTM D790 |
| Flexural Strength | 190 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 213 | °C | |
| 1.8 MPa, Unannealed | 205 | °C | |
| Melting Temperature | 216 | °C | |
| CLTE - Flow | 5.5E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec | UL 746 | ||
| 0.810 mm | 65.0 | °C | |
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C | |
| RTI Imp | UL 746 | ||
| 0.810 mm | 65.0 | °C | |
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C | |
| RTI Str | UL 746 | ||
| 0.810 mm | 65.0 | °C | |
| 1.50 mm | 65.0 | °C | |
| 3.00 mm | 65.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 12 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | 500 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.810 mm) | HB | UL 94 | |
| Oxygen Index | 24 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 218 to 235 | °C | |
| Middle Temperature | 246 to 257 | °C | |
| Front Temperature | 246 to 268 | °C | |
| Nozzle Temperature | 246 to 268 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 60.0 to 93.3 | °C | |
| Injection Pressure | 34.5 to 138 | MPa | |
| Screw Speed | 60 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 19HT40-0.002 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| AKROMID® C3 GF 40 1 black (4658) | AKRO-PLASTIC GmbH | Nylon 66/6 | AKROMID® |
| APEX® 82-E254-K | Teknor Apex Company | PVC, Flexible | APEX® |
| KPOL-NYLON K-NY6/27B | KPOL Chem Co. | Nylon 6 | KPOL-NYLON |
| ISPLEN® PP 030 G1E | REPSOL | PP Homopolymer | ISPLEN® |