| 50% glass fibres reinforced injection moulding grade for technical articles with high strength |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.55 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.8 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 15500 | 12100 | MPa | ISO 527-2/1 |
| Tensile Stress 1(Break, 23°C) | 230 | 160 | MPa | ISO 527-2/5 |
| Tensile Strain 2(Break, 23°C) | 3.0 | 5.0 | % | ISO 527-2/5 |
| Flexural Stress 3(23°C) | 315 | 280 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 4 | ISO 179/1eA | |||
| -30°C | 21 | 25 | kJ/m² | |
| 23°C | 21 | 26 | kJ/m² | |
| Charpy Unnotched Impact Strength 5 | ISO 179/1eU | |||
| -30°C | 95 | 100 | kJ/m² | |
| 23°C | 100 | 110 | kJ/m² | |
| Notched Izod Impact Strength 6 | ISO 180/1A | |||
| -30°C | 18 | 21 | kJ/m² | |
| 23°C | 20 | 23 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 7 | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 8 | 222 | -- | °C | ISO 3146 |
| CLTE 9 | DIN 53752 | |||
| Flow | 1.4E-5 | -- | cm/cm/°C | |
| Transverse | 5.6E-5 | -- | cm/cm/°C | |
| Maximum Service Temperature | IEC 216 | |||
| 20000 hrs | 110 | -- | °C | |
| some hours | 200 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 10 | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity 11 | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity 12 | 4.20 | 6.10 | IEC 60250 | |
| Dissipation Factor 13(1 MHz) | 0.014 | 0.14 | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm 14 | HB | -- | ||
| 1.60 mm 15 | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | 80x10x4 mm |
| 4 . | 80x10x4 mm |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 110x10x4 mm |
| 8 . | 10 K/min, Compound for moulding |
| 9 . | >=10x10x4 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| 12 . | 80x80x1 mm |
| 13 . | 80x80x1 mm |
| 14 . | 125x13x0.8 mm |
| 15 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Staramide AK8 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Sylvin 8934-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| HiFill® PA6/6 GF40 UV L BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Lupoy® ER5001RF | LG Chem Ltd. | PC+ABS | Lupoy® |
| Sylvin 8200-88 Yellow 433 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |