Hiprolon® 11 ECN Gray H8L
| Category: | Nylon 1012 , Polyamide 1012 |
| Manufacturer: | Arkema |
| Trademark: | Hiprolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RfP4oN_Hiprolon-11-ECN-Gray-H8L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hiprolon ® 11 ECN Gray H8L is a polyamide produced from a renewable source. This gray coloured grade is designed for extrusion and recommended for cable sheathing application. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (235°C/5.0 kg) | 5.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 72 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 45.0 | MPa | |
| Break | 61.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 22 | % | |
| Break | > 200 | % | |
| Flexural Modulus | 1170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 190 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA 1012, KHL, 22-010 | ISO 1874 | |
| Renewable Carbon Conent | > 42 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Melt Temperature | 210 to 260 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIPLOY® E3010 | Sumitomo Chemical Co., Ltd. | PESU | SUMIPLOY® |
| Ultramid® B36 LN | BASF Corporation | Nylon 6 | Ultramid® |
| ADDILENE J 120 M20 | ADDIPLAST | PP Copolymer | ADDILENE |
| Hostacom ERC 2020N C12616 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Osterlene® PPH20NA | Osterman & Company | PP Homopolymer | Osterlene® |