AEI SX545:CM540U

Category:	XLPE , Crosslinked Polyethylene
Manufacturer:	AEI Compounds Limited
Trademark:	AEI
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	RfCyVH_AEI-SX545-CM540U.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Low smoke, low-toxicity, halogen-free, flame-retardant, silane crosslinkable compound for insulation of LV cables and sheathing of all types of cables

This is a low smoke, low fume, fire retardant silane crosslinkable compound, which can be processed like a thermoplastic material at high output rates. The graft component SX545 is mixed with the crosslinking catalyst CM540U generally in the ratio 95:5.

The compound combines good mechanical, electrical and fire retardant properties to meet demanding insulation specifications such as BS7211. This compound can also be used for sheathing of cables which require high levels of fire retardancy.

General Information
Additive	Flame retardancy
Features	Irritant gas low to no Low smoke Low toxicity Crosslinkable Halogen-free Flame retardancy
Uses	Flame Retardant Insulation Flame Retardant Jacketing Low voltage insulation Cable sheath Wire and cable applications
Agency Ratings	BS 7211 EC 1907/2006 (REACH)
RoHS Compliance	RoHS compliance
Forms	Particle
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Density	1.49	g/cm³	BS 2782 620A

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress	12.0	MPa	IEC 60811-1-1
Tensile Strain (Break)	140	%	IEC 60811-1-1

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength (135°C, 168 hr)	20	%	IEC 60811-1-2
Change in Tensile Strain at Break (135°C, 168 hr)	-15	%	IEC 60811-1-2

Thermal	Nominal Value	Unit	Test Method
Deformation- K=1 (100°C)	30	%	IEC 60811-3-1
Cold bending (-30°C)	pass		IEC 60811-1-4
Thermoset ¹			IEC 60811-2-1
Elongation under load, 20N/cm² : 200°C	50	%	IEC 60811-2-1
Permanent elongation after cooling	0.0	%	IEC 60811-2-1
Temperature index	260	°C	ISO 4589-3

Electrical	Nominal Value	Unit	Test Method
Conduction rate- of gases	13.0	µS/cm	IEC 60754-2
Insulation resistance constant- Ki (90°C)	0.29	Mohms·km	IEC 60502

Flammability	Nominal Value	Unit	Test Method
Corrosive gases in flue gas- pH	4.60		IEC 60754-2
Smoke Density		%	ASTM D2843

Additional Information	Nominal Value	Unit	Test Method
Halogen Acid Gas Evolution		%	IEC 60754-1

Extrusion	Nominal Value	Unit
Head Temperature	160	°C

Flammability	Nominal Value	Unit	Test Method
Oxygen Index	32	%	ISO 4589-2

Additional Information	Nominal Value	Unit	Test Method
Crosslinking or Cure: A satisfactory cure can be obtained either by immersion in hot water or exposure to low pressure steam at a temperature up to 65°C.

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	130	°C
Cylinder Zone 2 Temp.	140	°C
Cylinder Zone 3 Temp.	145	°C
Cylinder Zone 4 Temp.	150	°C
Die Temperature	160	°C

Extrusion instructions
Many modern thermoplastic extruders will process the material, although a screw designed to give good homogenisation without excessive shear (which could cause unacceptable increases in melt temperature) should be used. An extruder with an L/D ratio (length/diameter) of 15-24 and an extruder screw with a compression ratio 1.2:1 are recommended.

Note Message
1 .	Cure assessment by hot set test (forced cured at 80°C in water)

Resin Grade	Manufacturer	Category	Trademark
Sumikon® PM-9625	Sumitomo Bakelite Co., Ltd.	Phenolic	Sumikon®
Sylvin 8225-75 Black	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Aegis® H135MP	Honeywell	Nylon 6	Aegis®
MARPOL® LDF 703-SB	Marco Polo International, Inc.	LDPE	MARPOL®
Syncure™ MB150	PolyOne Corporation	XLPE	Syncure™