LNP™ THERMOCOMP™ OC006 compound
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RbkZZp_LNPTHERMOCOMPOC006compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP OC006 is a compound based on PPS - Linear resin containing Carbon Fiber. Added features include : Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound OC1006L Product reorder name: OC006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 26600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 213 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 22500 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 298 | MPa | ISO 178 |
| -- 4 | 250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 5(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6(23°C) | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, unannealed, 64.0mm span | 280 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 267 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 6.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 4.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 - 316 | °C | |
| Middle Temperature | 321 - 332 | °C | |
| Front Temperature | 332 - 343 | °C | |
| Processing (Melt) Temp | 316 - 321 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MERICAN® -9010 | Huachang Polymer Co., Ltd. | Polyester Alloy | MERICAN® |
| ACCUTECH™ CP0436C30L1 | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| AMTOPP BTP23 | Inteplast Group | PP, Unspecified | AMTOPP |
| PELPRENE™ P48U | TOYOBO America, Inc. | TPEE | PELPRENE™ |
| ISOTHANE® 1685A-E2 | Great Eastern Resins Industrial Co., Ltd. (GRECO) | TPU-Polyether | ISOTHANE® |