BESTNYL SE30VI02AS08
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Rak4Gu_BESTNYL-SE30VI02AS08.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 black lubrified with 30% glass fibre reinforcement and friction treated, shows good mechanical properties, it makes it ideal for injection pieces with a final application that involves any kind of mechanical effort and / or mobile pieces under any kind of friction. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.50 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.80 | % | ISO 62 |
| Ash Content | 30 | % | Internal Method |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 81 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9400 | MPa | ISO 527-2 |
| Tensile Stress | 172 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 72 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 250 | °C | ISO 75-2/B |
| Vicat Softening Temperature | > 260 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Electric Strength | 32 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Processing (Melt) Temp | 270 to 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PE 4020R (20405) | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| NYCOA Polyamide 512 HS | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| COBIFOAM 0 | M&G Gruppo Mossi & Ghisolfi | PET | COBIFOAM |
| ELASTEL™ PROF-S1 | HELLENIC CABLES S.A. | EPDM | ELASTEL™ |
| PENTAMID B GV60 H natural | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |