Matrixx FPP1A10CC
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | The Matrixx Group, Inc. |
| Trademark: | Matrixx |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RaEG0m_Matrixx-FPP1A10CC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Matrixx FPP1A10CC is a polypropylene material, and the filler is 10% glass fiber reinforced material. This product is available in North America and is processed by injection molding. The main features of the Matrixx FPP1A10CC are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 - 0.60 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 48.3 | MPa | ASTM D638 |
| Flexural Modulus - Tangent | 2480 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 149 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 129 | °C | ASTM D648 |
| RTI | 65.6 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 104 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 199 - 243 | °C | |
| Middle Temperature | 199 - 243 | °C | |
| Front Temperature | 199 - 243 | °C | |
| Processing (Melt) Temp | 199 - 243 | °C | |
| Mold Temperature | 15.6 - 65.6 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | < 0.345 | MPa | |
| Screw Speed | 20 - 60 | rpm | |
| Cushion | 6.35 - 12.7 | mm |
| Injection instructions |
|---|
| Drying not normally required |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ LA60 | Mando Advanced Materials Co., Ltd. | Nylon 66 | SEPAZ™ |
| Spartech Polycom PP5120 D92 | Spartech Polycom | PP Homopolymer | Spartech |
| SUPREME GPPS SC203EL | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| Hyundai EP PA66 LD630 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| Sylvin 8380-75 Brown 7438 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |