HiFill® TPU/I CF10
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RXXBMR_HiFill-TPU-I-CF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® TPU/I CF10 is a Thermoplastic Polyurethane Elastomer (Polyether) (TPU-Polyether) product filled with carbon fiber. It can be processed by injection molding and is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 103 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | % | ASTM D638 |
| Flexural Modulus | 6210 | MPa | ASTM D790 |
| Flexural Strength | 155 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 to 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 to 1.0E+5 | ohms·cm | ASTM D257 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ NN-40CF/000 FRV0 Natural | PolyOne Corporation | Nylon 66 | Stat-Tech™ |
| Hylac® GP74 | Ravago Manufacturing Americas, LLC | ABS | Hylac® |
| Sylvin 5225-92 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Elastocon® 2855 | Elastocon TPE Technologies | TPE | Elastocon® |
| LNP™ THERMOCOMP™ WC006 compound | SABIC Innovative Plastics | Polyester, TP | LNP™ THERMOCOMP™ |